堵盖用TPE
TPE-1250A 物性表
1250A是热塑性弹性体(TPE),具有良好的强度、较低的压缩永久变形、突出的耐候性。
1250A is a Thermoplastic elastomer(TPE). It is featured by excellent strength, compression set and weatherability.
物理特性 Physical Property |
典型数值Typical Value |
测试依据 Test Method |
肖氏硬度,邵氏A,5秒 Hardness, ShA,5 seconds delayed |
50 | ASTM D2240 |
密度Density |
1.05g/cm3 | ASTM D792 |
比重Specific gravity |
1.05 | ASTM D792 |
拉伸强度Tensile strength | 3.5MPa | ASTM D412 |
拉伸应力(在100%时)Tensile Modulus @100% |
0.8MPa | ASTM D412 |
断裂伸长率Elongation at break |
400% | ASTM D412 |
撕裂强度,C 型Tear strength, Die C |
18.0 KN/m | ASTM D624 |
IRM903号油,体积膨胀率(1250C,70小时)IRM903 oil, Vol swell(2820F/1250C,70hr) |
/ | ASTM D471 |
压缩永久变形(700C,22hr) Compression set (700C,22hr) |
35 % | ASTM D395 |
耐臭氧性(臭氧浓度:500hrs/100pphm) Ozone resistance (500hrs/100pphm ozone conc.) |
A级 Good |
ASTMD1149 |
收缩率 Shrinkage |
1.2-1.8 % | ASTM D955 |
TPE-1250A工艺建议 Processing Recommendation
注塑Injection molding |
典型数值Typical value |
干燥温度Drying temp. | 70-800C |
干燥时间Drying time | 3-4 hr |
后段温度Rear temp. | 170~180°C |
中段温度Middle temp. | 180~200°C |
前段温度Front temp. | 180~200°C |
出口温度Nozzle temp. | 190~200°C |
加工(熔体)温度Melt temp. | 190~200°C |
模具温度Mold temp. | 10~50°C |
背压Back pressure | 0.3-0.7Mpa |
螺杆转速Screw speed | 100 ~200 rpm |
更多产品信息,请访问宁波瀚科网站www.ningbonexlink.com或者咨询宁波瀚科销售经理。